Fast exposing dual cure emulsion.
Low viscosity and high solid makes flat profile emulsion surface.
Less smudge/bleeding, excellent print performance.
Excellent mesh adhesion and encapsulation properties, durable printing.
Excellent solvent resistance and easy to reclaim, extended re-use of screen mesh.
Superb resolution and sharp image definition for the fine image reproduction.
Suitable for solvent based inks, UV inks.
Suitable for fine line graphic image, PCB patterns, nameplate and ceramic tiles using plastisol.
Viscosity: Approx. 4000-4500 mPa･s, 25℃
Solid Contents: Approx. 40-42%
Packaging Standards: 1kg set, 5kgs set.
Contact us for custom packaging.
Solvent Resistance Rating
※24 hours swelling/absorption test results.
|Screen mesh, Color||E.O.M (μm)||2Kw Metal Halide lamp
|Polyester 120/cm (300/inch) w||7-9||90-100 sec.|
|Polyester 110/cm (300/inch) w||10-12||105-115 sec.|
|Polyester 100/cm (250/inch) w||7-9||100-110 sec.|
|Polyester 90/cm (250/inch) w||10-12||115-125 sec.|
|Polyester 77/cm (200/inch) w||7-9||105-115 sec.|
|Polyester 80/cm (200/inch) w||10-12||120-130 sec.|
※The above is for guideline purposes only, kindly to use a gray scale exposure calculator to identify optimal exposure time.
Wash, degrease and dry screen mesh. Remove grease and foreign contaminants with MSP cleanser.
Dissolve attached Diazo powder with water amount for 10% of emulsion volume. Do not use warm water.
Pour Diazo solution into emulsion and mix it well. Prior to use, let mixed emulsions settle for one day. Or for immediate use, filter it with screen mesh 100/cm or higher.
Avoid excessive temperature for drying screens.
Coat emulsion slowly in order to prevent air bubbles.
Dry coated screen completely before exposure. Drying temperatures up to 40℃ (104℉).
Keep the emulsion in a cool and UV light safe area.
Recommended to filter remaining emulsion with screen mesh before pouring it back into the container to remove any dust, foreign substances and air bubbles.